Research towards gold nanopartices integral property
EUGENE, US: University of Oregon chemists have captured fundamental new insights about the stability of ligand-stabilized gold nanoparticles. According to the scientists, the information could help to maintain a desired, integral property in nanoparticles used in electronic devices, where stability is important, or to design them so they readily condense into thin films for such things as inks or catalysts in electronic or solar devices.
The research focused on nanoparticles less than two nanometre in diameter (the smallest studied to date) to better understand structural stability of these tiny particles being engineered for use in electronics, medicine and other materials. Whether a nanoparticle needs to remain stable or condense depends on how they are being used. Those used as catalysts in industrial chemical processing or quantum dots for lighting need to remain intact; if they are precursors for coatings in solar devices or for printing ink, nanoparticles need to be unstable so they sinter and condense into a thin mass.
For their experiments, doctoral student Beverly L Smith and James E Hutchison, who holds the Lokey-Harrington Chair in Chemistry at the University of Oregon produced gold nanoparticles in four well-controlled sizes, ranging from 0.9 nanometre to 1.5 nanometre, and analyzed ligand loss and sintering with thermogravimetric analysis and differential scanning calorimetry, and examined the resulting films by scanning electron microscopy and X-ray photoelectron spectroscopy. As the nanoparticles were heated at 5 degrees Celsius per minute, from room temperature to 600 degrees Celsius, the nanoparticles began to transform near 150 degrees Celsius.
The researchers found that smaller nanoparticles have better structural integrity than larger-sized particles that have been tested. In other words, Hutchison said, they are less likely to lose their ligands and bind together. “If you have unstable particles, then the property you want is fleeting. Either the light emission degrades over time and you’re done, or the metal becomes inactive and you’re done. In that case, you want to preserve the function and keep the particles from aggregating,” added Hutchison.
“We want solution precursors that can lead to inorganic thin films for use in electronics and solar industries. In this case, we want to know how to keep our nanoparticles or other precursors stable enough in solution so that we can work with them, using just a tiny amount of additional energy to make them unstable so that they condense into a film - where the property that you want comes from the extended solid that is generated, not from the nanoparticles themselves,” said Hutchison.
According to Hutchison, the research identified weak sites on nanoparticles where ligands might pop off. If only a small amount do so, separate nanoparticles are more likely to come together and begin the sintering process to create thin films. “That’s a really stabilizing effect that, in turn, kicks out all these ligands on the outside. The surface area decreases quickly and the particles get bigger, but now all the extra ligands gets excluded into the film and then, over time, the ligands vaporize and go away,” added Hutchison.
The coming apart, however, is a ‘catastrophic failure’ if protecting against sintering is the goal. It may be possible to use the findings, to explore ways to strengthen nanoparticles, such as developing ligands that bind in at least two sites or avoiding volatile ligands.
The process, as studied, produced porous gold films. “A next step might be to study how to manipulate the process to get a more dense film if that is desired. Understanding how nanoparticles respond to certain conditions, such as changing temperatures may help researchers reduce waste in the manufacturing process,” said Hutchison.